Semi-permanent acrylic self-adhesive, ready-for-use, for protective films (PE). Cross-linking recommended to obtain optimum cohesion characteristics.
|
|
|
|
Water base pressure sensitive adhesive acrylic polimeric base. High cohesion. Suitable for formulating removable pressure sensitive adhesives resistant on plasticised PVC..
|
|
|
|
Water base pressure sensitive adhesive acrylic polymeric base. High cohesion, suitable for formulating pressure sensitive adhesives with very high resistance on plasticised PVC and also for repositionable stickers on paper.
|
|
|
|
Polymeric base with very good cohesion, used for formulating removable and permanent adhesives, with or without addition of tackifiers. Good resistance to plasticizers.
|
|
|
|
Semi-permanent water based acrylic pressure sensitive adhesive. Suitable for protective films and "application tapes".It can be crosslinked by addition of 1-3% Icaplink X3 or Icaplink X5.
|
|
|
|
Semi-permanent water based acrylic pressure sensitive adhesive. Suitable for protective films and "application tapes".It can be crosslinked by addition of 1-3% Icaplink X3 or Icaplink X5.
|
|
|
|
Water based acrylic polimeric base pressure sensitive adhesive. High tack and shear. Dried films are colourless and very transparent. Suitable for application on polypropylene tapes.
|
|
|
|
Removable water based acrylic pressure sensitive adhesive. For building tapes and protective films. Good water resistance and easy removable from many surfaces. It can be crosslinked with 1-3% Icaplink X3 or Icaplink X5.
|
|
|
|
Solvent based acrylic pressure sensitive adhesive, cross linkable with isocuanic adducts at 0,1-0,7%. Base for removable and semi-permanent adhesives. 40% solids content in ethyl acetate.
|
|
|
|
Crosslinking agent for solvent-based acrylic adhesives.
|
|
|
|
Aliphatic polyisocianate easily dispersible in water based PU and acrylic dispersions. The amount to apply is dependant on the structure of the polymer and is ranging from 1% to 5%. Pot-life is influenced by the reactivity of the system and by pH.
|
|
|
|
Crosslinking agent for products in aqueous dispersion containing carboxylic groups. Suggested amount to use: from 1% to 5% of polymer. Pot-life is dependant on pH (longer at high pH) and temperature. Never use after 24 hours from mixing.
|
|